Ultra Low Cement Castable
|
|
|
Properties
|
|
INDEX
|
ITEMS
|
CUC-180
|
CUC-170
|
CUC-160
|
CUC-150
|
CUC-140
|
Max Service
Temperature/℃
|
|
1800
|
1700
|
1600
|
1500
|
1400
|
Refractoriness, ℃
|
|
≥1790
|
≥1790
|
≥1790
|
__
|
__
|
Volume Density, g/cm3(110
℃,24h
)
|
|
≥2.8
|
≥2.7
|
≥2.4
|
≥2.3
|
≥2.20
|
%( 1500 ℃,3h)Linear change after reheating %
|
|
± 1.0
|
± 1.0
|
± 1.0
|
(1400℃,3h) ± 1.0
|
(1400℃,3h) ± 1.0
|
C.C.R. Strength,MPa
|
110 ℃,24h
|
≥25
|
≥25
|
≥25
|
≥25
|
≥25
|
C.C.R. Strength,MPa
|
1500 ℃,3h
|
≥50
|
≥50
|
≥50
|
≥40 ( 1400ºC,
3h)
|
≥40 ( 1400 ºc, 3h)
|
MPa
(1400℃,1h)
Bending Resistance after Hesting
|
|
≥4.5
|
≥3.0
|
≥3.0
|
≥1.5
|
≥1.0
|
Al2 O3 , %
|
|
≥85
|
≥80
|
≥70
|
≥60
|
≥45
|
Water Adding,%
|
|
4~6
|
5~6
|
6~8
|
6~8
|
6~8
|
|
|
|
|
|
|