Low Cement Castable
|
|
Properties
|
|
INDEX
|
ITEMS
|
|
CLC-170
|
CLC-160
|
CLC-150
|
CLC-140
|
CLC-140A
|
CLC-130
|
Max Service
Temperature/℃
|
1700
|
1600
|
1500
|
1400
|
1400
|
1300
|
Refractoriness, ℃
|
≥1790
|
≥1790
|
≥1790
|
__
|
__
|
__
|
Volume Density, g/cm3(110
℃,24h
)
|
≥2.7
|
≥2.5
|
≥2.3
|
≥2.2
|
≥2.1
|
≥2.1
|
( 1500 ℃,3h)Linear Change after Reheating,%
|
± 1.0 (1500ºC)
|
± 1.0 (1500ºC)
|
± 1.0 (1400ºC)
|
± 1.0 (1300ºC)
|
± 1.0 (1300ºC)
|
± 1.0 (1300ºC)
|
/MPa(110 ℃,24h) C.C.R. Strength,Mpa
|
≥40
|
≥40
|
≥35
|
≥30
|
≥35
|
≥30
|
/Mpa 3h C.C.R. Strength,MPa/MPa
3 h
|
≥50
( 1500 ºc)
|
≥50
(1500 ºc)
|
≥50
(1500 ºc)
|
≥50
(1500 ºc)
|
≥50
(1500 ºc)
|
≥50
(1500 ºc)
|
Al2 O3 , %
|
≥65
|
≥60
|
≥55
|
≥50
|
≥42
|
≥37
|
Water Adding,%
|
6~7
|
6~8
|
7~9
|
7~9
|
7~9
|
7~9
|
|
|
|